Nanoporous composites prepared by a combination of SBA-15 with Mg–Al mixed oxides. Water vapor sorption properties

• Amaury Pérez-Verdejo,
• Alvaro Sampieri,
• Heriberto Pfeiffer,
• Mayra Ruiz-Reyes,
• Juana-Deisy Santamaría and
• Geolar Fetter

Beilstein J. Nanotechnol. 2014, 5, 1226–1234, doi:10.3762/bjnano.5.136

• nanostructured mesoporous composites by interconnecting and combining SBA-15 with mixed oxides derived from a calcined Mg–Al hydrotalcite. Two different Mg–Al hydrotalcite addition procedures were implemented, either after or during the SBA-15 synthesis (in situ method). The first procedure, i.e., the post

• might be utilized as as acid-base catalysts, adsorbents, sensors or storage nanomaterials. Keywords: calcined Mg–Al hydrotalcite; nanoporous composites; SBA-15; vapor sorption; Introduction Multifunctional nanomaterials are designed to satisfy specific ranged sets of performance requirements. The

• prepared composites and the SBA-15 show H1 hysteresis loops due to the N2 capillary condensation. It also denotes that the pores present a cylindrical form and narrow size distribution (Figure 1B). Calcined Mg–Al hydrotalcite shows a N2 adsorption–desorption isotherm with a wide hysteresis loop (H3 type